Featured Products
Products See More
  Fiberglass Filament Yarn
  Geogrids/Geonets
  Fiberglass Insect Screen
  Glass Textile Wallcovering
  Fiberglass Mats
  Chopped Strands
  Woven Roving
  Fiberglass Mesh
  Drywall Joint Tape
  Glass Fiber Fabric/Cloth
  Fiberglass Roving
  Fiberglass Sleeving
  Geotextiles
  Geocells/Geowebs
  Geomembranes/Pond Liners
  Geocomposites
  Other Geosynthetics/Earthwork
  Engineering Fiber
  Geosynthetic Clay Liners/GCLs
  Geomat
  Drainage Net
  PVC Corner Mesh/Corner Bead
  Silicone Baking Mat
  Polyester Roofing Fabric
  Machines
 
Fiberglass
Geosynthetics
 
 
 
 
Featured Products  
Bentonite Mat

 

Input Date::[2010/9/1 13:20:30]    From:Fibtex Co.,Ltd.

 

Bentonite Mat are an established sealing product in the geoenvironmental industry. They are used in landfill caps and base liner applications under roads, railways, secondary containment for above ground tank farms, as well as within various other containment structures such as dams, canals, ponds, rivers and lakes. They are also used for waterproofing of buildings and other similar structures.

Rolled out like a carpet to provide a durable impermeable liner, geosynthetic clay liners consist of a layer of high swelling sodium bentonite, sandwiched between two geotextiles. by different techniques, manufactured GCL, Geosyntech, is mechanically bonded by needlepunching from one nonwoven geotextile through the bentonite to the other nonwoven or woven geotextile.


Sodium Bentonite is a naturally occurring clay with hundreds of uses. Comprising mainly montmorillonite, a layered clay mineral with broad flat platelets which are ideally shaped to provide a hydraulic barrier. Sodium ions located between these platelets allow water to hydrate the bentonite in an absorption reaction that results in the bentonites swelling characteristics. swells when contacted with water approximately 900% by volume or 700% by weight. When hydrated under confinement, the bentonite swells to form a low permeability clay layer with the equivalent hydraulic protection of several feet of compacted clay.


This swelling allows the bentonite to seal around penetrations, giving the GCL self sealing characteristics. During hydration, a confined layer of dry bentonite changes into a dense monolithic mass with no observable individual particles. A fully hydrated sodium bentonite layer can have a hydraulic conductivity of approximately one hundred times lower than a typical compacted clay liner (CCL).


Because of their low hydraulic conductivity, GCLs are used mainly as a replacement for thick, difficult to build, compacted clay liners to provide a barrier to liquids and gases.
Permathene supply and install a range of GCL's from light to heavy grades. These are high performance environmental liner comprised of geosynthetic carrier components integrated with a layer of low permeability sodium bentonite. The rolls are supplied in wide widths, minimising seams. Installation is fast.

 

[Technical Specification of GCL]

 

Material Property
Test Method
Test Results  
Bentonite Swell Index
ASTM-D-5890
24mL/2g min
Bentonite Fluid Loss
ASTM-D-5891
18mL max
Bentonite Mass/Area2
ASTM-D-5993
5.0kg/m2 min
GCL Grab Strength
ASTM-D-4632
400N max
GCL Peel Strength
ASTM-D-4632
65.8N min
GCL Index Flux
ASTM-D-5887
1x10-8m3/m2/sec max
GCL Permeability
ASTM-D-5887
5x10-9cm/sec max
GCL Hydrated Internal Shear Strength
ASTM-D-5321
24kPa typical 

 

 